{"id":7892,"date":"2026-09-28T13:56:56","date_gmt":"2026-09-28T05:56:56","guid":{"rendered":"https:\/\/www.bomissteel.com\/product\/dx53d-z-galvanized-steel-coil-en-10346\/"},"modified":"2026-09-28T14:56:58","modified_gmt":"2026-09-28T06:56:58","slug":"dx53d-z-galvanized-steel-coil-en-10346","status":"publish","type":"product","link":"https:\/\/www.bomissteel.com\/tr\/product\/dx53d-z-galvanized-steel-coil-en-10346\/","title":{"rendered":"DX53D+Z Galvanized Steel Coil – EN 10346 Deep Drawing Grade"},"content":{"rendered":"

Introduction<\/h2>\n

DX53D+Z is the deep drawing grade of the EN 10346<\/a> hot-dip family, and it lands where most forming work actually sits. BOMIS supplies it as coil or cut sheet, Z100 to Z275, 0.30 to 3.00 mm thick, with the mill certificate on every coil.<\/p>\n

\u00f6zellikler<\/h2>\n

The DX53D+Z is specified with a minimum elongation of 30 % at A80 and a yield range of 140 to 260 MPa and this combination is the focus of the grade. DX54D<\/a> draws deeper, takes it a bit further, but costs lower strength for the extra formability, so a part that is formed twice and then has to carry load generally does better here. Think brackets, duct sections and panel stiffeners instead of a single deep cup.<\/p>\n

The carbon\u00a0is limited to 0.12% and titanium to 0.30% resulting in a substrate that is stable enough for repeat production. This matters when the formed face remains visible because zinc stretches with the steel at the bend instead of flaking. Zinc boils at a relatively low temperature, so the coated steel is scheduled for welding, not the bare sheet.<\/p>\n

Specifications<\/h2>\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n
\u015eartname<\/th>\nDetaylar<\/th>\n<\/tr>\n<\/thead>\n
Standart<\/td>\nEN 10346 (+Z, +ZF, +ZA, +ZM)<\/td>\n<\/tr>\n
Malzeme numaras\u0131<\/td>\n1.0951<\/td>\n<\/tr>\n
Not t\u00fcr\u00fc<\/td>\nDeep drawing, DX5xD family<\/td>\n<\/tr>\n
Akma mukavemeti Re<\/td>\n140 - 260 MPa<\/td>\n<\/tr>\n
\u00c7ekme mukavemeti Rm<\/td>\n270 - 380 MPa<\/td>\n<\/tr>\n
Uzama A80<\/td>\n30% min<\/td>\n<\/tr>\n
Kal\u0131nl\u0131k<\/td>\n0.30 \u2013 3.00 mm<\/a><\/td>\n<\/tr>\n
Geni\u015flik<\/td>\n600 \u2013 1500 mm<\/td>\n<\/tr>\n
Bobinin i\u00e7 \u00e7ap\u0131<\/td>\n508 mm \/ 610 mm<\/td>\n<\/tr>\n
\u00c7inko kaplama k\u00fctlesi<\/td>\nZ100 \u2013 Z275 g\/m\u00b2<\/td>\n<\/tr>\n
Coating types<\/td>\n+Z, +ZF, +ZA, +ZM<\/td>\n<\/tr>\n
Par\u0131lt\u0131<\/td>\nS\u0131f\u0131r, k\u00fc\u00e7\u00fclt\u00fclm\u00fc\u015f, normal<\/a><\/td>\n<\/tr>\n
Y\u00fczey i\u015fleme<\/td>\nKrom i\u00e7ermeyen pasivasyon, krom kaplamal\u0131, parmak izi \u00f6nleyici, ya\u011fl\u0131 \/ ya\u011fs\u0131z<\/td>\n<\/tr>\n
Karbon s\u0131n\u0131r\u0131<\/td>\n0.12%<\/td>\n<\/tr>\n
Manganez maksimum de\u011feri<\/td>\n0.60%<\/td>\n<\/tr>\n
Fosfor \/ k\u00fck\u00fcrt maksimum<\/td>\n0.10% \/ 0.045%<\/td>\n<\/tr>\n
Titanyum Max<\/td>\n0.30%<\/td>\n<\/tr>\n
ADEDI<\/td>\nSpesifikasyona g\u00f6re 16 metrik ton<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Uygulamalar<\/h2>\n

DX53D+Z goes where a part is formed hard and then has to stay rigid. Appliance plants run it for drums and liners, automotive tier suppliers for inner panels and fuel tank shells, and building work for profiled cladding<\/a> and ducting. EN 10346 sets no r90 or n90 value on this grade, so if your die depends on a measured anisotropy figure rather than a tryout, DX54D is the honest answer.<\/p>\n